Damage Tolerance Evaluation of Adhesively Laminated TitaniumSource: Journal of Engineering Materials and Technology:;1983:;volume( 105 ):;issue: 003::page 182Author:W. S. Johnson
DOI: 10.1115/1.3225641Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: Basic damage tolerance properties of Ti-6Al-4V titanium plate can be improved by laminating thin sheets of titanium with adhesives. Compact tension and center-cracked tension specimens made from thick plate, thin sheet, and laminated plate (six plies of thin sheet) were tested. The fracture toughness of the laminated plate was 39 percent higher than the monolithic plate. The laminated plate’s through-the-thickness crack growth rate was about 20 percent less than that of the monolithic plate. The damage tolerance life of the surface-cracked laminate was 6 to over 15 times the life of a monolithic specimen.
keyword(s): Titanium , Tension , Thickness , Adhesives , Laminates , Fracture (Materials) AND Fracture toughness ,
|
Collections
Show full item record
| contributor author | W. S. Johnson | |
| date accessioned | 2017-05-08T23:15:40Z | |
| date available | 2017-05-08T23:15:40Z | |
| date copyright | July, 1983 | |
| date issued | 1983 | |
| identifier issn | 0094-4289 | |
| identifier other | JEMTA8-26893#182_1.pdf | |
| identifier uri | http://yetl.yabesh.ir/yetl/handle/yetl/97176 | |
| description abstract | Basic damage tolerance properties of Ti-6Al-4V titanium plate can be improved by laminating thin sheets of titanium with adhesives. Compact tension and center-cracked tension specimens made from thick plate, thin sheet, and laminated plate (six plies of thin sheet) were tested. The fracture toughness of the laminated plate was 39 percent higher than the monolithic plate. The laminated plate’s through-the-thickness crack growth rate was about 20 percent less than that of the monolithic plate. The damage tolerance life of the surface-cracked laminate was 6 to over 15 times the life of a monolithic specimen. | |
| publisher | The American Society of Mechanical Engineers (ASME) | |
| title | Damage Tolerance Evaluation of Adhesively Laminated Titanium | |
| type | Journal Paper | |
| journal volume | 105 | |
| journal issue | 3 | |
| journal title | Journal of Engineering Materials and Technology | |
| identifier doi | 10.1115/1.3225641 | |
| journal fristpage | 182 | |
| journal lastpage | 187 | |
| identifier eissn | 1528-8889 | |
| keywords | Titanium | |
| keywords | Tension | |
| keywords | Thickness | |
| keywords | Adhesives | |
| keywords | Laminates | |
| keywords | Fracture (Materials) AND Fracture toughness | |
| tree | Journal of Engineering Materials and Technology:;1983:;volume( 105 ):;issue: 003 | |
| contenttype | Fulltext |