On Higher-Order Crack-Tip Fields in Creeping Solids

Abstract

In view of the near-tip constraint effect imposed by the geometry and loading configuration, a creep fracture analysis based on C* only is generally not sufficient. This paper presents a formulation of higher-order crack-tip fields in steady power-law creeping solids which can be derived from an asymptotic development of near-tip fields analogous to that of Sharma and Aravas and Yang et al. for elastoplastic bodies. The higher-order fields are controlled by a parameter named A2*, similar as in elastoplasticity, and a second loading parameter, σ∞. By means of the scaling properties for power-law materials, it is shown that A2* for a flat test specimen is independent of the loading level. Finally, we carry out small-strain finite element analyses of creep in single-edge notched tension, centered crack panel under tension, and single-edge notched bending specimens in order to determine the corresponding values of A2* for mode I cracks under plane-strain conditions. [S0021-8936(00)01202-2]