| contributor author | J. Ahmad | |
| contributor author | J. Purbolaksono | |
| contributor author | A. K. Kadir | |
| contributor author | M. M. Rahman | |
| date accessioned | 2017-05-09T00:46:33Z | |
| date available | 2017-05-09T00:46:33Z | |
| date copyright | December, 2011 | |
| date issued | 2011 | |
| identifier issn | 0094-9930 | |
| identifier other | JPVTAS-28553#061402_1.pdf | |
| identifier uri | http://yetl.yabesh.ir/yetl/handle/yetl/147413 | |
| description abstract | This paper presents failure investigation on reheater pendent SA213-T22 tubes through visual inspections, steam-side scale and tube wall thickness measurements, metallurgical examinations, and creep analysis. The investigations were carried out following subsequent tube failures of the reheater pendent region of a boiler unit. Interaction event of significant internal scale formation causing the higher metal temperature and external scale exfoliation as a result of high-temperature corrosion is identified to cause the failure of the reheater pendent tube. Prevention actions are recommended to avoid similar failures in the future. | |
| publisher | The American Society of Mechanical Engineers (ASME) | |
| title | Failure Investigation on Reheater Pendent Tubes Due to External Scale Exfoliation and Internal Scale Formation | |
| type | Journal Paper | |
| journal volume | 133 | |
| journal issue | 6 | |
| journal title | Journal of Pressure Vessel Technology | |
| identifier doi | 10.1115/1.4004561 | |
| journal fristpage | 61402 | |
| identifier eissn | 1528-8978 | |
| keywords | Creep | |
| keywords | Temperature | |
| keywords | Metals | |
| keywords | Incrustations | |
| keywords | Corrosion | |
| keywords | Failure | |
| keywords | Steam | |
| keywords | Wall thickness | |
| keywords | High temperature | |
| keywords | Rupture | |
| keywords | Thickness | |
| keywords | Measurement | |
| keywords | Boilers AND Inspection | |
| tree | Journal of Pressure Vessel Technology:;2011:;volume( 133 ):;issue: 006 | |
| contenttype | Fulltext | |