| description abstract | The precipitation characteristics of tetrahedrally close-packed (TCP) phases during the welding and the subsequent solution annealing process of Alloy 22 1 1∕2in. thick plate double-U prototypical welds are investigated. Electron backscatter diffraction was used to provide large scale microstructural observation of the weld cross section, and scanning electron microscopy was used to map the location of the TCP phases. Analysis shows that TCP precipitation occurs congruent to the weld passes, with the solution annealing reducing the sizes of coarser precipitates. | |
| publisher | The American Society of Mechanical Engineers (ASME) | |
| title | Second Phase Precipitation in As-Welded and Solution Annealed Alloy 22 Welds | |
| type | Journal Paper | |
| journal volume | 128 | |
| journal issue | 4 | |
| journal title | Journal of Pressure Vessel Technology | |
| identifier doi | 10.1115/1.2349578 | |
| journal fristpage | 644 | |
| journal lastpage | 647 | |
| identifier eissn | 1528-8978 | |
| keywords | Alloys | |
| keywords | Annealing | |
| keywords | Welded joints | |
| keywords | Precipitation AND Welding | |
| tree | Journal of Pressure Vessel Technology:;2006:;volume( 128 ):;issue: 004 | |
| contenttype | Fulltext | |