| dc.description.abstract | Abstract. Nickel-rich single-crystal (SC) layered oxides are promising cathode candidates for next-generation lithium-ion batteries (LIBs) owing to their high energy density and structural robustness against intergranular cracking. However, their intrinsic surface reactivity with liquid electrolytes accelerates parasitic reactions at the cathode–electrolyte interphase (CEI), leading to transition-metal dissolution, gas generation, and impedance buildup. In this work, we synthesized SC-LixNi0.9Mn0.05Co0.05O2 (NMC9055, 1 ≤ x ≤ 1.2) using a eutectic-assisted method and investigated interface stabilization strategies. A nickel-deficient LixNi0.6Mn0.2Co0.2O2 (NMC622, 1 ≤ x ≤ 1.2) coating was applied via evaporation-based deposition to suppress CEI degradation pathways. Structural and compositional analyses confirmed uniform shell formation and preserved particle integrity. Half-cell electrochemical testing against lithium metal revealed ∼10% higher capacity retention and improved reversibility compared with pristine SC NMC9055, particularly under high-voltage operation. These results highlight the critical role of controlled surface chemistry in mitigating CEI instability in nickel-rich SC cathodes, offering a pathway toward enabling durable high-energy LIBs. | |