| dc.description.abstract | Abstract. Electrically induced bearing damage (EIBD) is a growing concern in electric drivetrains, where electrical discharge currents generate localized pitting that accelerates wear and premature failure. While ionic liquids (ILs) have shown promise as lubricant additives due to their natural physical adsorption, strong capabilities of tribofilm formation, and high molecular tunability, their role in mitigating EIBD is little known. This gap is especially evident because lubricant viscosity and film thickness affect discharge behavior, and additive performance in these regimes has not been well explored. In this study, tribological tests were performed using a ball-on-disk pure rolling-contact system under an applied voltage on polyalphaolefin oils of three viscosities (4, 10, and 150 cSt measured at 100 °C), with and without the addition of a phosphonium-phosphate IL. Surface damage was analyzed using scanning electron microscopy (SEM) and stylus profilometry. Damage quantification was based on pit morphology analysis of SEM images. The results provide new insights into how oil viscosity governs the discharge behavior and how an IL additive could influence the pit formation. While viscosity seems to play a significant role, an IL additive shows potential to reduce EIBD and deserves further study. | |