Fracture Mechanism of Steel Q370 under Strong Corrosion Based on Surface Morphology
Publisher: American Society of Civil Engineers
Abstract: A comprehensive investigation, including experimental research, finite-element analysis, and theoretical derivation, was thoroughly carried out on the steel Q370 under strong corrosion to study its fracture mechanism ...
Ductility Degradation of Weathering Steel Q345 after Exposure to Hydrochloric-Acid Corrosion Dependent on Pitting Damage
Publisher: ASCE
Abstract: This paper investigated stress flow in weathering steel Q345 after strong acid corrosion. In total, 27 specimens were immersed in 36% industrial hydrochloric acid for 0, 1, 2, 4, 8, 12, 24, 48, and 72 h, respectively. ...