RISThe Effect of Water Flow Rate Upon the Environmentally Assisted Cracking Response of a Low-Alloy Steel
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: The effect of water flow rate upon the environmentally assisted cracking (EAC) response of a high-sulfur ferritic steel was studied at a temperature of 243°C. In contrast to earlier studies ...
Corrosion Fatigue Crack Growth in Clad Low-Alloy Steels—Part I: Medium-Sulfur Forging Steel
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: Corrosion fatigue crack propagation tests were conducted on a medium-sulfur ASTM A508-2 forging steel overlaid with weld-deposited alloy EN82H cladding. The specimens featured semi-elliptical surface ...
Corrosion Fatigue Crack Growth in Clad Low-Alloy Steels—Part II: Water Flow Rate Effects in High-Sulfur Plate Steel
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: Corrosion fatigue crack propagation tests were conducted on a high-sulfur ASTM A302-B plate steel overlaid with weld-deposited Alloy EN82H cladding. The specimens featured semi-elliptical surface ...
Overload Effects on Fatigue Damage of Wire-Rope Pendants
Publisher: The American Society of Mechanical Engineers (ASME)