| description abstract | Abstract. The contribution is concerned with the influence of bristle-blasting on texture, chemical status, and corrosion of aluminum (AA6082) substrates in synthetic and real seawater. The performance of an offshore epoxy coating, applied onto the substrates, is also investigated. Bristle-blasting generated substrates with a low level of contamination and with a rather regular surface texture. It complied with requirements for offshore use in terms of substrate roughness and coating adhesion. The filiform corrosion tests delivered useful results. The cyclic corrosion test duration (3000 h), however, was too short, and the degradation was negligible. The coating performance was also evaluated during two years in real marine outdoor exposure in the splash zone and the tidal zone in a North Sea location (Helgoland); the results were compared with the laboratory test results. For the first time, acceleration factors were calculated for the filiform laboratory test. The test generated very high acceleration factors, which depended on the location of the specimens during outdoor site testing. | |