Abstract: The variable hot ductility of wholly austenitic Type 347 steel was found to be associated with the variable temperature of formation of a liquid phase (liquation temperature) in the microstructure ...

Abstract: Specimens of 1.25 Cr–0.5 Mo steel which had been exposed for prolonged times at 1000 F under ASME Boiler and Pressure Vessel Code allowable stresses were rupture tested in order to evaluate ...

Abstract: Experimental heats of Type 304 steel, compositionally balanced to be wholly austenitic and thus simulate the material used to produce seamless superheater tubing, were prepared to determine the ...