RISHigh-Temperature Oxidation Behavior of 214Cr-1Mo Steel in Air–Part 2: Scale Growth, Metal Loss Kinetics, and Stress Enhancement Factors During Creep Testing
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: The oxide-scale growth and metal loss kinetics during oxidation in air of 2 1/4 Cr-1 Mo steel were studied at 600, 700, and 800°C for times up to 1000 h, with cylindrical specimens ...
High-Temperature Oxidation Behavior of 214Cr-1Mo Steel in Air—Part 1: Gain of Mass Kinetics and Characterization of the Oxide Scale
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: The oxidation behavior of 214Cr-1Mo steel was studied at 600, 700 and 800°C for a sequence of times up to 1000 h, using cylindrical specimens of the material, similar to testpieces used ...
Structural Integrity of a Standpipe Component in a Petrochemical Catalytic Cracking Unit: Part 2—Assessment of Embrittlement Effects
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: During a shutdown for general maintenance of a catalytic cracking unit, intergranular cracks were observed to occur during welding of the regenerator’s standpipe component manufactured from 2 1/4 ...
Structural Integrity of a Standpipe Component in a Petrochemical Catalytic Cracking Unit: Part 1—Assessment of Creep Rupture Properties
Publisher: The American Society of Mechanical Engineers (ASME)
Abstract: During a shutdown for general maintenance of a catalytic cracking unit, intergranular cracks were observed to occur during welding of the regenerator’s standpipe component manufactured from 2 1/4 ...